Colossal thermoelectric power in charge ordered lanthanum calcium manganites (La0.5Ca0.5MnO3)

Lija K. Joy, S. Shanmukharao Samatham, Senoy Thomas, V. Ganesan, Salim Al-Harthi, A. Liebig, M. Albrecht, M. R. Anantharaman*

*Corresponding author for this work

Research output: Contribution to journalArticlepeer-review

28 Citations (Scopus)


Lanthanum calcium manganites (La0.5Ca0.5MnO3) with a composition close to charge ordering, synthesized by high energy ball milling, was found to exhibit colossal thermoelectric power. Thermoelectric power (TEP) data was systematically analyzed by dividing the entire temperature range (5 K-300 K) into three different regimes to explore different scattering mechanisms involved. Mandal's model has been applied to explain TEP data in the region below the Curie temperature (TC). It has been found that the variation of thermoelectric power with temperature is pronounced when the system enters the charge ordered region at T < 200 K. For temperatures lower than 120 K, due to the co-existence of charge ordered state with a spin-glass state, the variation of thermoelectric power is maximum and exhibited a peak value of -80 mV/K at 58 K. This has been explained by incorporating Kondo properties of the spin-glass along with magnon scattering. FC-ZFC magnetization measurements indicate the existence of a glassy state in the region corresponding to a maximum value of thermoelectric power. Phonon drag contribution instead of spin-glass contribution is taken into account to explain TEP in the region 120 K < T < TC. Mott's polaronic contribution of charge carriers are considered to interpret TEP in the high temperature region (T > TC). The optimal Mn4+-Mn3+ concentration in charge ordered La0.5Ca0.5MnO3 was examined by X-ray Photoelectron Spectroscopy analysis which confirms the charge ordered nature of this compound.

Original languageEnglish
Article number213701
JournalJournal of Applied Physics
Issue number21
Publication statusPublished - Dec 7 2014

ASJC Scopus subject areas

  • Physics and Astronomy(all)


Dive into the research topics of 'Colossal thermoelectric power in charge ordered lanthanum calcium manganites (La0.5Ca0.5MnO3)'. Together they form a unique fingerprint.

Cite this