The influence of mechanical milling and subsequent calcination on the formation of lithium ferrites

H. M. Widatallah, F. J. Berry*

*المؤلف المقابل لهذا العمل

نتاج البحث: المساهمة في مجلةمقالمراجعة النظراء

39 اقتباسات (Scopus)

ملخص

The influence of ball milling and subsequent calcination of a 2.5:1 molar mixture of α-Fe2O3 and Li2CO3 on the formation of lithium ferrites has been investigated. Premilling was found to considerably lower the temperature at which the lithium ferrites LiFeO2 and LiFe5O8 are formed. A β-to-α-phase transition in LiFe5O8 was found to take place on cooling from ca. 1000°C depending on the milling history and cooling regime.

اللغة الأصليةEnglish
الصفحات (من إلى)230-236
عدد الصفحات7
دوريةJournal of Solid State Chemistry
مستوى الصوت164
رقم الإصدار2
المعرِّفات الرقمية للأشياء
حالة النشرPublished - 2002
منشور خارجيًانعم

ASJC Scopus subject areas

  • ???subjectarea.asjc.2500.2504???
  • ???subjectarea.asjc.2500.2503???
  • ???subjectarea.asjc.3100.3104???
  • ???subjectarea.asjc.1600.1606???
  • ???subjectarea.asjc.1600.1604???
  • ???subjectarea.asjc.2500.2505???

بصمة

أدرس بدقة موضوعات البحث “The influence of mechanical milling and subsequent calcination on the formation of lithium ferrites'. فهما يشكلان معًا بصمة فريدة.

قم بذكر هذا