Hf doping effect on hard magnetism of nanocrystalline Zr 18-xHfxCo82 ribbons

I. A. Al-Omari*, W. Y. Zhang, Lanping Yue, R. Skomski, J. E. Shield, X. Z. Li, D. J. Sellmyer

*المؤلف المقابل لهذا العمل

نتاج البحث: المساهمة في مجلةArticleمراجعة النظراء

15 اقتباسات (Scopus)


The effects of substituting Zr by Hf on the structural and the magnetic properties of the nanocrystalline rapidly solidified Zr18-xHf xCo82 ribbons (x = 0, 2, 4, and 6) have been studied. X-ray diffraction and thermomagnetic measurement results indicated that upon rapid solidification processing four magnetic phases occur: rhombohedral Zr 2Co11, orthorhombic Zr2Co11, hcp Co, and cubic Zr6 Co23 phases. Microstructure analysis results showed the reduction in the percentage of the soft-magnetic phase (Co) compared to the hard-magnetic phase (Zr2Co11 (rhombohedral)) with the increase in the Hf concentration. All the samples under investigation have ferromagnetic nature, at 4.2 K and at room temperature. The coercive force (Hc) and the saturation magnetization (Ms) are found to linearly increases with x (x ≤ 2), then Hc slightly increases and Ms slightly decreases with increasing x. The maximum energy product (BH})max at room temperature is found to increases with increasing x reaching a maximum value for x = 4. The magnetocrystalline anisotropy parameter of these samples are calculated to be K = 1.1 MJ/m 3 and independent of Hf concentration. The above results indicate that the replacement of Zr by Hf improves the hard-magnetic properties of this class of rear-earth-free nanocrystalline permanent magnet materials.

اللغة الأصليةEnglish
رقم المقال6559021
الصفحات (من إلى)3394-3397
عدد الصفحات4
دوريةIEEE Transactions on Magnetics
مستوى الصوت49
رقم الإصدار7
المعرِّفات الرقمية للأشياء
حالة النشرPublished - 2013

ASJC Scopus subject areas

  • ???subjectarea.asjc.2500.2504???
  • ???subjectarea.asjc.2200.2208???


أدرس بدقة موضوعات البحث “Hf doping effect on hard magnetism of nanocrystalline Zr 18-xHfxCo82 ribbons'. فهما يشكلان معًا بصمة فريدة.

قم بذكر هذا