Anisotropy of optical constants of YBCO

D. G. Walmsley*, A. Sellai, P. G. McCafferty, P. Dawson, C. C. Smyth, T. Morrow, W. G. Graham

*المؤلف المقابل لهذا العمل

نتاج البحث: المساهمة في مجلةArticleمراجعة النظراء

1 اقتباس (Scopus)


Otto configuration attenuated total reflection (ATR) measurements of the excitation of surface plasmons in the infrared have been carried out on YBCO films deposited on MgO (100) substrates. The dielectric constants for YBCO at 3.392 μm are determined to be -10+15i for c-axis material. The anisotropic nature of the cuprate is seen from films with other orientations: nearly a-axis material has constants of 4.0+7.0i. It is thus not metallic in its optical response along the c-axis which lies parallel to the substrate plane. Ellipsometric measurements in the visible on c-axis material point to a maximum surface plasmon energy of 1 eV.

اللغة الأصليةEnglish
الصفحات (من إلى)943-946
عدد الصفحات4
دوريةJournal of Superconductivity
مستوى الصوت7
رقم الإصدار6
المعرِّفات الرقمية للأشياء
حالة النشرPublished - ديسمبر 1994
منشور خارجيًانعم

ASJC Scopus subject areas

  • ???subjectarea.asjc.2500.2504???
  • ???subjectarea.asjc.3100.3104???
  • ???subjectarea.asjc.3100.3101???


أدرس بدقة موضوعات البحث “Anisotropy of optical constants of YBCO'. فهما يشكلان معًا بصمة فريدة.

قم بذكر هذا