The influence of ball milling and subsequent sintering of a 3:5 molar mixture of Y2O3 and α-Fe2O3 on the formation of nanocrystalline Y3Fe5O12 (YIG) particles is studied. Pre-milling the mixture for 100 h lowers the onset temperature at which the material forms to 900°C which is 200°C lower than that reported when a similar mixture of reactants was premilled for shorter times. A single-phased nanocrystalline Y3Fe5O 12 phase develops as a sole product when the pre-milled mixture is heated at 1,000°C (12 h). This temperature is ~300-400°C lower than those used to prepare the material conventionally. The bulk and surface crystal structure of the nanoparticles is studied with X-ray diffraction, Mössbauer spectroscopy, Atomic Force Microscope (AFM) and X-ray photoelectron spectroscopy.
اللغة الأصلية | English |
---|---|
الصفحات (من إلى) | 87-92 |
عدد الصفحات | 6 |
دورية | Hyperfine Interactions |
مستوى الصوت | 183 |
رقم الإصدار | 1-3 |
المعرِّفات الرقمية للأشياء | |
حالة النشر | Published - أبريل 2008 |
ASJC Scopus subject areas
- ???subjectarea.asjc.3100.3107???
- ???subjectarea.asjc.3100.3106???
- ???subjectarea.asjc.3100.3104???
- ???subjectarea.asjc.1600.1606???