Magnetic anisotropy in ilmenite-hematite solid solution thin films grown by pulsed laser ablation

K. Rode*, R. D. Gunning, R. G.S. Sofin, M. Venkatesan, J. G. Lunney, J. M.D. Coey, I. V. Shvets

*المؤلف المقابل لهذا العمل

نتاج البحث: المساهمة في مجلةمقالمراجعة النظراء

12 اقتباسات (Scopus)

ملخص

Ferromagnetic thin films of the ilmenite-hematite solid solution Fe2-xTixO3 with x=0.6 and x=0.8 have been grown on (0 0 1) sapphire substrates. X-ray diffraction analysis reveals that the films are single phase with the ilmenite (R over(3, -)) crystal structure. Strong easy-plane anisotropy is observed for the two films, which are nominally n or p type with K1=-8×106 J m-3 for x=0.6 and -11×106 J m-3 for x=0.8 at T=4 K. The trigonal splitting of the 5T2g energy level of Fe2+ is inferred to be 0.11 eV, and the zero-field splitting parameter D to be equal to 15 K.

اللغة الأصليةEnglish
الصفحات (من إلى)3238-3241
عدد الصفحات4
دوريةJournal of Magnetism and Magnetic Materials
مستوى الصوت320
رقم الإصدار23
المعرِّفات الرقمية للأشياء
حالة النشرPublished - ديسمبر 2008
منشور خارجيًانعم

ASJC Scopus subject areas

  • ???subjectarea.asjc.2500.2504???
  • ???subjectarea.asjc.3100.3104???

بصمة

أدرس بدقة موضوعات البحث “Magnetic anisotropy in ilmenite-hematite solid solution thin films grown by pulsed laser ablation'. فهما يشكلان معًا بصمة فريدة.

قم بذكر هذا